The color stability of resin cements plays a key role in the achievement of esthetically-pleasant restorations. Resin luting materials can be mainly divided into two main classes: adhesive (relying on previous application of adhesive systems) or self-adhesive (also known as one-step cements). The different chemical compositions determine their physio-mechanical characteristics which, in turns, influence their color stability. To evaluate the color variations of different dual-cured resin cements after water aging, 80 disc-shaped specimens (15 mm in diameter and 1.2 mm thick) were obtained from the following resin cements (n = 10): (1) Maxcem Elite Universal, MCU (Kerr); (2) RelyX Universal, RXU (3M); (3) Calibra Ceram, CAL (Dentsply); (4) Multilink, MUL (Ivoclar-Vivadent); (5) Panavia V5, PAN (Kuraray); (6) Calibra Universal, CUN (Dentsply); (7) SpeedCEM Plus, SCP (Ivoclar); and (8) Panavia SA, PSA (Kuraray). After light-polymerization, the specimens were measured with a spectrophotometer and CIELab* values were recorded. The specimens were then placed in a digitally controlled thermostatic water bath at 60° for 30 days and afterwards the color measurements were repeated. Color differences were calculated for each specimen before and after water-aging procedures with ΔEab formula and the data were statistically analyzed (p < 0.05). The type of cement statistically influenced the ΔEab (p < 0.05), with MCU showing the lowest color variations (4.3 ± 0.7) whereas RXU and PSA the highest (16.9 ± 1.6 and 16.8 ± 1.2, respectively). No differences were observed between CAL, CUN and SCP (p = 0.05). Color stability is related to the chemical composition of the resinous luting materials, thus material dependent.

Color Stability of Resin Cements after Water Aging / Mazzitelli, C.; Paolone, G.; Sabbagh, J.; Scotti, N.; Vichi, A.. - In: POLYMERS. - ISSN 2073-4360. - 15:3(2023). [10.3390/polym15030655]

Color Stability of Resin Cements after Water Aging

Paolone G.
Secondo
;
2023-01-01

Abstract

The color stability of resin cements plays a key role in the achievement of esthetically-pleasant restorations. Resin luting materials can be mainly divided into two main classes: adhesive (relying on previous application of adhesive systems) or self-adhesive (also known as one-step cements). The different chemical compositions determine their physio-mechanical characteristics which, in turns, influence their color stability. To evaluate the color variations of different dual-cured resin cements after water aging, 80 disc-shaped specimens (15 mm in diameter and 1.2 mm thick) were obtained from the following resin cements (n = 10): (1) Maxcem Elite Universal, MCU (Kerr); (2) RelyX Universal, RXU (3M); (3) Calibra Ceram, CAL (Dentsply); (4) Multilink, MUL (Ivoclar-Vivadent); (5) Panavia V5, PAN (Kuraray); (6) Calibra Universal, CUN (Dentsply); (7) SpeedCEM Plus, SCP (Ivoclar); and (8) Panavia SA, PSA (Kuraray). After light-polymerization, the specimens were measured with a spectrophotometer and CIELab* values were recorded. The specimens were then placed in a digitally controlled thermostatic water bath at 60° for 30 days and afterwards the color measurements were repeated. Color differences were calculated for each specimen before and after water-aging procedures with ΔEab formula and the data were statistically analyzed (p < 0.05). The type of cement statistically influenced the ΔEab (p < 0.05), with MCU showing the lowest color variations (4.3 ± 0.7) whereas RXU and PSA the highest (16.9 ± 1.6 and 16.8 ± 1.2, respectively). No differences were observed between CAL, CUN and SCP (p = 0.05). Color stability is related to the chemical composition of the resinous luting materials, thus material dependent.
2023
color stability
dual-cure
resin cement
self-adhesive cement
water aging
File in questo prodotto:
File Dimensione Formato  
polymers-15-00655.pdf

accesso aperto

Tipologia: PDF editoriale (versione pubblicata dall'editore)
Licenza: Creative commons
Dimensione 1.08 MB
Formato Adobe PDF
1.08 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.11768/137936
Citazioni
  • ???jsp.display-item.citation.pmc??? 4
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 8
social impact